CVD Synthetic Diamond Over 5 Carats Identified by GIA
/This 5.19 ct CVD synthetic diamond (10.04 × 9.44 × 6.18 mm, with J-equivalent color and VS2-equivalent clarity) is the largest GIA has identified to date. Photo by Johnny Leung and Tony Leung.
Originally published by GIA on October 5th 2016
Chemical vapor deposition (CVD) technology has accelerated over the last several years, and the rapidly improving techniques have produced large, high-quality near-colorless and colorless synthetic diamonds. Two samples over 3 carats were reported in early 2016 as the largest CVD synthetics. GIA recently tested a CVD-grown synthetic diamond that weighed over 5 carats, marking a significant milestone.
The 5.19 ct cushion modified brilliant measuring 10.04 × 9.44 × 6.18 mm was submitted to GIA’s Hong Kong laboratory for grading service. The stone was not disclosed as a synthetic diamond. Using the lab’s standard screening and testing processes, it was identified as CVD synthetic. Following examination, a GIA Identification Report was issued and the stone was inscribed on the girdle with the report number and the words “Laboratory Grown,” following GIA’s protocols for undisclosed synthetics.
This is the largest CVD synthetic diamond GIA has examined to date, and the largest reported in the jewelry industry. It had J-equivalent color grade and VS2-equivalent clarity, comparable to a high-quality natural counterpart. Natural-looking internal inclusions such as needles and clouds were the major features. Strong graining and a fracture in the table were also clearly observed under the microscope. The black inclusions that are often found in synthetic diamond, were not found in this CVD specimen. This stone could have easily been mistakenly identified as natural based on microscopic examination alone. This case highlights the importance of using advanced spectroscopic instruments as well as conventional gemological techniques to ensure an accurate identification. Link to Original Article
I will be writing more on the subject of lab grown diamonds in the coming days. If you are interested in the subject I would encourage you to join my mailing list!